Wear pads for timing-based surface film servo heads

ABSTRACT

A thin film magnetic recording head is provided with a tape bearing surface that has magnetically isolated channels while still providing a maximum continuous surface area with which to engage the media. This can be accomplished by providing spaces in the magnetically permeable thin film that are large enough to prevent cross-talk between the channels, but small enough to prevent significant interference with the moving media. Alternatively, magnetically impermeable thin film spacers can be provided to magnetically isolate each of the channels. The spacers are generally even with the magnetically permeable thin film so as to provide a continuous media-bearing surface.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation in part of application Ser.No. 09/475,420, filed Dec. 30, 1999, which is herein incorporated byreference in its entirety.

FIELD OF THE INVENTION

This invention relates generally to magnetic recording heads and moreparticularly to thin film magnetic recording heads having wear pads tominimize media degradation and head wear.

BACKGROUND OF THE INVENTION

While a variety of data storage mediums are available, magnetic taperemains a preferred forum for economically storing large amounts ofdata. In order to facilitate the efficient use of this media, magnetictape will have a plurality of data tracks extending in a transducingdirection of the tape. Once data is recorded onto the tape, one or moredata read heads will read the data from those tracks as the tapeadvances, in the transducing direction, over the read head. It isgenerally not feasible to provide a separate read head for each datatrack, therefore, the read head(s) must move across the width of thetape (in a translating direction), and center themselves over individualdata tracks. This translational movement must occur rapidly andaccurately.

In order to facilitate the controlled movement of a read head across thewidth of the media, a servo control system is generally implemented. Theservo control system consists of a set of dedicated servo tracksembedded in the magnetic media and a corresponding servo read head(which may be one of the standard read heads, temporarily tasked toservo functions) which correlates the movement of the data read heads.

The servo track contains data, which when read by the servo read head isindicative of the relative position of the servo read head with respectto the magnetic media in a translating direction. In one type oftraditional amplitude based servo arrangement, the servo track wasdivided in half. Data was recorded in each half-track, at differentfrequencies. The servo read head was approximately as wide as the widthof a single half-track. Therefore, the servo read head could determineits relative position by moving in a translating direction across thetwo half-tracks. The relative strength of a particular frequency ofservo signal would indicate how much of the servo read head was locatedwithin that particular half-track. The trend toward thinner and thinnermagnetic tape layers causes amplitude modulation problems with this andother amplitude based heads. That is, as the thickness of the magneticlayer decreases, normal variations on the surface represent a muchlarger percentage variation in the magnetic layer, which willdramatically affect the output signal.

Recently, a new type of servo control system was created which allowsfor a more reliable positional determination by reducing the amplitudebased servo signal error traditionally generated by debris accumulationand media thickness non-uniformity. U.S. Pat. No. 5,689,384, issued toAlbrecht et al. on Nov. 19, 1997, introduces the concept of a timingbased servo pattern on a magnetic recording head.

In a timing based servo pattern, magnetic marks (transitions) arerecorded in pairs within the servo track. Each mark of the pair will beangularly offset from the other. For example, a diamond pattern has beensuggested and employed with great success. The diamond will extendacross the servo track in the translating direction. As the tapeadvances, the servo read head will detect a signal or pulse generated bythe first edge of the first mark. Then, as the head passes over thesecond edge of the first mark, a signal of opposite polarity will begenerated. Now, as the tape progresses, no signal is generated until thefirst edge of the second mark is reached. Once again, as the head passesthe second edge of the second mark, a pulse of opposite polarity will begenerated. This pattern is repeated indefinitely along the length of theservo track. Therefore, after the head has passed the second edge of thesecond mark, it will eventually arrive at another pair of marks. At thispoint, the time it took to move from the first mark to the second markis recorded. Additionally, the time it took to move from the first mark(of the first pair) to the first mark of the second pair is similarlyrecorded.

By comparing these two time components, a ratio is determined. Thisratio will be indicative of the position of the read head within theservo track, in the translating direction. As the read head moves in thetranslating direction, this ratio will vary continuously because of theangular offset of the marks. It should be noted that the servo read headis relatively small compared to the width of the servo track, so that acontinuously variable timing difference 15 provided as the servo readhead traverses the servo track. Because position is determined byanalyzing a ratio of two time/distance measurements, taken relativelyclose together, the system is able to provide accurate positional data,independent of the speed (or variance in speed) of the media.

Of course, once the position of the servo read head is accuratelydetermined, the position of the various data read heads can becontrolled and adjusted with a similar degree of accuracy on the samesubstrate. Namely, the various read heads are fabricated on the samesubstrate with a known spacing between them. Hence knowing the locationof one allows for a determination of the location of the remainder ofthe read heads.

When producing magnetic tape (or any other magnetic media) the servotrack is generally written by the manufacturer. This results in a moreconsistent and continuous servo track, over time. To write the timingbased servo track described above, a,magnetic recording head bearing theparticular angular pattern as its gap structure, must be utilized. As itis advantageous to minimize the amount of tape that is dedicated toservo tracks, to allow for increased data storage, and it is necessaryto write a very accurate pattern, a very small and very precise servorecording head element must be fabricated.

Two types of servo recording heads having a timing based pattern areknown. The first is a pure thin film head, such as that disclosed byAboaf et al. in U.S. Pat. No. 5,572,392, issued on Nov. 5, 1996. With apure thin film head, all of the components of the head are created fromlayering different materials, as thin films, on an inert substrate. Forexample, the magnetic core, and the windings and any barrier materialsare formed by producing thin films. Such a head has very low inductance;however, it is extremely difficult to manufacture. To date, pure thinfilm heads are generally not utilized for time based servo heads and arenot seen as a practical way to produce such a magnetic head.

A very different type of recording head is taught by Albrecht et al. inthe '384 patent. This second type of head is referred to herein as asurface film or surface thin film head and is illustrated as 100, inFIG. 18. The surface film head 100 includes two C-shaped ferrite blocks110, 112 that are bonded to a ceramic member 114 that extends the entirewidth of the head 100. A surface is then polished flat or contoured andprepared for this film deposition. A magnetically permeable thin film116 is deposited over an upper surface of the ferrite blocks 110, 112and the exposed upper portion of the ceramic member 114. The thin film116 is shown much larger than it would actually be, respective to theother elements. Gaps 118 are formed in the thin film 116, in anappropriate timing based pattern. Windings 120 are wrapped and areelectrically driven to drive flux around the ferrite core and throughthe thin film 116 (in the direction of arrow A). The flux leaks from thegaps 118 and writes media passing over it.

Such a surface film head has a high inductance due to the large volumeof ferrite forming the core and a high reluctance “back-gap”, due to theseparation of the ferrite block 110, 112 by the ceramic member 114, onthe underside of the head (i.e., opposite the thin film 116). The sizeand dimensions of the head are determined by the end usecharacteristics. For example, the width of the head 100 is defined bythe width of the media; i.e., a head that is 19 mm wide is appropriateto support a tape that is 12.5 mm wide. The ceramic member 114 must bethick enough to allow the proper angular patterns 118 to be locatedabove it and is approximately 0.012″ in the known versions of theAlbrecht et al. head, produced by IBM. The length of the head must besufficient to support the media as it travels over the tape bearingsurface and the depth (especially of the ferrite cores) must besufficient to allow appropriate windings to be attached and to allow thehead to be securely fixed in a head mount.

With the surface film head, flux is forced to travel through amagnetically permeable thin film that bridges a generally magneticallyimpermeable barrier between sections of the core. The writing gap islocated within this thin film and the magnetic flux is expected to leakfrom this gap and write the media. The width of the ferrite is muchlarger than the sum of the channel widths. Hence, there is a largeamount of unnecessary ferrite inductance. In other words, as a result ofthe relatively large amount of extraneous ferrite, an unnecessarily highamount of inductance is created. Therefore, to produce a relativelysmall amount of flux leakage through a small gap in the thin film, veryhigh levels of voltage are required to generate sufficient magnetic fluxthroughout the relatively large core. This lowers the frequency responseof the head and increases the rise time of the writing pulses from thehead.

Therefore, there exists a need to provide efficient multi-channel timingbased head having the ability to individually and separately drive andcontrol each channel.

SUMMARY OF THE INVENTION

The present invention relates to a low inductance, high efficiencysub-gap, surface thin film magnetic recording head and a method offabricating the same.

A substrate consisting of a ceramic member, glass bonded between a pairof ferrite blocks is prepared. After the substrate is created, it isdiced to form a base from which a plurality of columns extend. Thenumber of columns will correspond to the eventual number of channels ina completed recording head. A ceramic block is prepared whichcorresponds to the dimensions of the substrate. Channels or notches arecut into the ceramic block so that the substrate columns engage them ina male/female relationship. The channels allow for the entirety of thecolumn to be accepted within the channel so that the base of thesubstrate flushly abuts the corresponding base of the ceramic block. Theceramic block is then adhered to the substrate. In particular, thecolumns of the substrate are glass bonded to the interior of thechannels in the ceramic block, thus forming a head member.

The top and bottom of the head member are then cut or ground to producea uniform block of alternating ceramic portions and substrate columnswherein each substrate column includes a sub-gap. A sufficient amount ofthe head member is cut or ground so that the substrate columns extendthrough the entire height of the remaining portion of the head member.During this process, the upper portion of the head member can beappropriately radiused, as it is this section which will become thetape-bearing surface of the writing head.

A separate winding may be provided for each channel, thus allowing eachchannel to be separately driven and controlled. Alternatively, anyparticular combination of channels can be tied together. When thechannels are timed and driven independently, sections of themagnetically permeable thin film must be removed between the channels.This prevents magnetic flux from passing from one channel to anotherthrough the thin film layer. It is the prevention of this cross talk,which allows the multi-channel head to have its channels drivenindependently in time or phase. To produce such isolation, sections ofthe thin film can be removed by ion milling, wet chemical etching, or byany other known process. Other techniques such as selective plating orselective sputtering could also be used. Alternatively, when thechannels are driven by a common winding, cross talk would notnecessarily be an issue. However, it would still be advantageous toremove the magnetically permeable material between the channels toachieve improved linearity and eliminate unwanted flux leakage aroundthe gaps.

In one embodiment, the present recording head provides a magneticallyimpermeable barrier between each channel so that actuation of onechannel will in no way interfere with any other channel in the head.Hence, a significant portion of the magnetic volume of the head layingbetween each channel has been replaced with a non-organic ceramicmaterial.

In another aspect of the present invention, the magnetically permeablethin film layer is optimally configured to complete a magnetic circuitfor each channel, while limiting mechanical interference of the filmwith the air bleed slots. Consideration must be given to the minimalrequirements for completing the circuit and the engagement of the mediaagainst a head having a non-planar surface while minimizing thecomplexity of providing the air bleed slots. In addition, when workingwith components of this scale, consideration must be given to theetching or milling technique utilized to impart and define the thin filmlayer so that mechanical shear or peeling of the film is not induced bythe tape's motion.

In yet another aspect of the present invention, the individual channelsare magnetically isolated from one another. To do so, the magneticallypermeable thin film that covers the tape-bearing surface of therecording head is sectioned. That is, sections of thin film are removedor only the appropriate pattern is deposited. Thus, thin film onlyexists where it is required to complete a magnetic circuit for eachchannel. Because of the relatively small dimensions of the thin filmlayer, it is possible to pass the media over a head that is madenon-continuous by the positioning of the magnetically conductivesections. That is, the spaces that are formed by the absence of the thinfilm layer are not an impediment to utilizing the head.

That being said, the spaces can cause the thin film to wear faster andcan possibly cause media degradation. To prevent these negative effectswhile still achieving magnetic channel separation, the present inventionutilizes wear pads. These wear pads can either be sections of themagnetically permeable thin film that fill in a majority of the spacesdescribed above or a magnetically impermeable material can actually bedeposited to fill in the spaces. Additionally, a combination of the twotechniques can also be utilized.

It is desirable to produce as close to a linear cross section aspossible. Thus, whatever material serves as the wear pad shouldapproximate the thin film layer in height and in its wearcharacteristics. That is, it would be undesirable to deposit a materialthat will be worn away quickly with respect to the wear of the thin filmlayer (or vice versa).

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side planar view of a substrate composed of ferrite blocksglass bonded to a ceramic member.

FIG. 2 is a top planar view of the substrate shown in FIG. 1.

FIG. 3 is a side view of the substrate of FIG. 1, diced into a pluralityof columns.

FIG. 4 is a side view of a ceramic block having a plurality of notches.

FIG. 5 is a side view of the ceramic block and the substrate bondedtogether.

FIG. 6 is a top view of the bonded substrate after the top and bottomhave been cut or ground.

FIG. 7 is a side view of the bonded substrate after the top and bottomhave been cut or ground.

FIG. 8 is a top view of a head assembly.

FIG. 9 is a side view of a head assembly.

FIG. 10 is an end sectional view taken about line 10-10.

FIG. 11 is an end sectional view taken about line 10-10 and having aback-bar attached.

FIG. 12 is a side view of a head assembly having a plurality ofback-bars affixed thereto, with coils individually wrapped about eachback-bars.

FIG. 13 is a side view of a head assembly having a plurality ofback-bars affixed thereto, with a single coil wrapped about all of theback-bars.

FIG. 14 is a head assembly showing a pattern of thin film.

FIG. 15 is a head assembly showing a thin film.

FIG. 16 is a head assembly showing various patterns of thin film.

FIG. 17 is a head assembly showing various patterns of thin film.

FIG. 18 is a perspective view in a prior art surface thin film magneticrecording head.

FIG. 19 is a side sectional view of a head substrate having uniform thinfilm layer extending substantially thereacross.

FIG. 20 is a side sectional view of a head substrate having substantialportions of the thin film layer removed so that large spaced or voidsare defined therebetween.

FIG. 21 is a side sectional view of a head substrate having wear padsformed from additional sections of the thin film layer so as to onlyform relatively small spaces.

FIG. 22 is a top planar view of the head substrate illustrated in FIG.21.

FIG. 23 is a side sectional view of a head substrate having a uniformthin film layer extending thereacross with predefined areas ofphotoresist on top of the thin film layer.

FIG. 24 is a side sectional view of the head substrate of FIG. 23 aftera process has removed the exposed sections of the thin film.

FIG. 25 is a side sectional view of the head substrate of FIG. 24 afterthe remaining photoresist has been removed.

FIG. 26 is a side sectional view of a head substrate having amagnetically permeable thin film disposed atop portions of the uppersurface with a magnetically impermeable thin film disposed atop theremaining portions.

FIG. 27 is a top planar view of the head substrate of FIG. 26.

FIG. 28 is a side sectional view of a head substrate having a uniformthin film layer extending thereacross with predefined areas ofphotoresist on top of the thin film layer.

FIG. 29 is a side sectional view of the head substrate of FIG. 28 aftera process has removed the exposed portions of the thin film.

FIG. 30 is a side sectional view of the head substrate of FIG. 29 aftera layer of magnetically impermeable thin film has been deposited.

FIG. 31 is a side sectional view of the head substrate of FIG. 30 afterthe photoresist has been removed.

FIG. 32 is a side sectional view of a head substrate having amagnetically permeable thin film disposed above each channel and amagnetically impermeable thin film disposed between each channel.

FIG. 33 is a top planar view of the head substrate of FIG. 32.

FIG. 34 is a side sectional view of a head substrate having amagnetically permeable thin film disposed across the upper surfacethereof and areas of photoresist patterned above each channel.

FIG. 35 illustrates the head substrate of FIG. 34 after the exposedportions of the thin film have been removed.

FIG. 36 illustrates the head substrate of FIG. 35 after a magneticallyimpermeable thin film has been deposited.

FIG. 37 illustrates the head substrate of FIG. 36 after the photoresisthas been removed.

FIG. 38 is a top, planar view of a portion of a head substrate.

FIG. 39 is a top, planar view of a portion of a head substrate.

FIG. 40 is a top, planar view of a portion of a head substrateillustrating a patterned thin film layer.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The present invention is a multi-channel head and method of making thesame. Referring to FIG. 1, a substrate 10 is created by glass bondingtwo C-shaped ferrite blocks 12 to a medially disposed ceramic member 14.The sizes, shapes and relative proportions of the ferrite blocks 12 andceramic member 14 may vary as dictated by the desired parameters of thecompleted recording head. Furthermore, the choice of materials may alsovary so long as blocks 12 remain magnetically permeable while member 14remains substantially magnetically impermeable. FIG. 2 is a top view ofthe substrate 10.

Referring to FIG. 3, substrate 10 is diced so as to form a plurality ofcolumns 16A-16E which remain adhered to base 18. Columns 16A-16E arealso shown by the dashed lines in FIG. 2, which illustrates how eachcolumn will have a ceramic portion (sub-gap) bonded between two ferritepoles. The dashed lines are merely illustrative of future columns, asthe substrate 10 in FIG. 2 has yet to be diced. As shown is FIG. 4, aceramic block 20, or slider, is cut to form a plurality of channels ornotches 22A-22E. The ceramic block 20 can be formed from bariumtitanate, or any other suitable magnetically impermeable material. Thenotches 22A-22E are cut to correspond with columns 16A-16E. As such, therelative size and shape of the columns 16A-16E and the notches 22A-22Eshould correspond; beyond that the selection of size and shape willsimply depend on the desired final parameters of the completed magnetichead.

As illustrated in FIG. 5, substrate 10 is mated with ceramic block 20.More specifically, columns 16A-16E are inserted into notches 22A-22Euntil the upper surface 26 of the base 18 of substrate 10 flushly meetsthe lower surface 28 of ceramic block 20. Subsequently, substrate 10 isadhered to ceramic block 20. This can be accomplished in any known way.In its most preferred form, substrate 10 is glass bonded to ceramicblock 20. To accomplish this, the substrate 10 is clamped or otherwisesecured to ceramic block 20, as shown in FIG. 5. Glass rods are placedinto the various notches 22A-22E, in a space left by the columns16A-16E. The assembly is then heated to a temperature sufficient to meltthe glass rods. This causes the melted glass to wick along the abuttingsides of the columns 16A-16E and the notches 22A-22E. Once allowed tocool, the glass hardens and bonds the members together.

The top and the bottom of this assembly are then cut or ground away toarrive at the head substrate 30 shown in FIGS. 6 and 7. From a top viewand moving left to right (as illustrated), head substrate 30 has aceramic portion 32A, which is a remainder of ceramic block 20. A bead ofglass 33 bonds ceramic portion 32A to ferrite column 16A. Mediallydissecting ferrite column 16A is a portion of ceramic member 14, whichis likewise glass bonded to ceramic portion 32A. It is to be understoodthat the portion of the non-magnetic ceramic member 14 extends throughthe entire length of the remaining ferrite column 16A, thus dividing itinto two magnetic poles. Glass bonds 33 likewise join ceramic portion32B between ferrite columns 16A and 16B. This pattern is repeated acrossthe head, with the number of ferrite columns 16A-16E, representing theeventual number of channels in the completed write head. FIG. 7 is aside view of head substrate 30 and illustrates that the ferrite columns16A-16E (with included sections of ceramic member 14, not visible inthis view) forming a sandwich pattern with the ceramic portions 32A-32F.As illustrated (in FIG. 4), the notches 22A-22E extend through theentire width of the ceramic block 20. Thus, the ferrite columns 16A-16Eare visible from a side view (FIG. 7).

Head substrate 30 is now ready to be formed into a completed magneticrecording head. To summarize the remainder of the fabrication, a slightradius or curvature is caused on the upper surface of the head substrate30. This step could occur when removing the top section from the bondedsubstrate 10 and ceramic block 20, or it could be done at this stage asa separate operation. The curvature is imparted to the head substrate 30because its upper surface will become the tape-bearing surface of thecompleted head. This curvature facilitates smooth contact with the mediaunder tension. A magnetically permeable thin film layer 34 is depositedacross the upper surface of the head substrate 30. Writing gaps 36 (FIG.8) are caused to be formed in this thin film 34, aligned with thevisible portion of ceramic member 14, or in other words, above thesub-gap. Alternatively, the head contour could be finished into agenerally flat surface having integrated negative pressure channels. Theuse of these various contours is known in the art.

Either prior to depositing the thin film or after, air bleed slots 38may be cut into head substrate 30 along the tape-bearing surface as isknown in the art. Once head substrate 30 has been fabricated into arecording head, magnetic tape will move across its upper surface in atransducing direction. Therefore, the air bleed slots 38 are cutperpendicular to the transducing direction. As the tape moves over therecording head at relatively high speed, air entrainment occurs. Thatis, air is trapped between the lower surface of the tape and the uppersurface of the recording head. As the tape moves over the recordinghead, the first air bleed slot encountered serves to skive off thetrapped air. The second and subsequent slots continue this effect, thusserving to allow the tape to closely contact the recording head. As thetape passes over the recording gaps 36, it is also held in place by theother air bleed slots 38 encountered on the opposite side of the gaps30.

FIG. 10 is an end, partially sectional view of head substrate 30 takenabout line 10-10. This figure illustrates the relationship between theferrite column 16A and the remaining portion of ceramic member 14. Thinfilm layer 34 is located on its upper surface and write gaps 36 arelocated immediately above the portion of ceramic member 14. Air bleedslots 38 are located on opposite side of ceramic member 14 and traversethe whole assembly. FIG. 11 illustrates the back-bar 40 of the presentinvention as it is attached to ferrite column 16A (again an end,partially sectional view taken about line 10-10). Back-bar 40 is asubstantially U-shaped ferrite block which is caused to abut each sideof the ferrite column 16A. The shape is chosen to efficiently complete amagnetic circuit and allows a coil 44 to be wound. The back-bar 40flushly abuts column 16A and is held in place by a bonding agent that isapplied at glue points 42. The use of back-bars 40 is advantageous inand of itself. In other words, using the back-bar 40 of the presentinvention will allow a better surface film head to be producedirrespective of the number of channels formed, or whether the combedstructure is utilized to achieve channel separation or to lower strayinductance by reducing the volume of magnetically permeable material inthe core.

By using the columned or combed structure, the volume of unnecessary ornon-useful magnetically permeable materials is greatly reduced, thusdecreasing the overall inductance of the head. As such, the frequencyresponse is dramatically increased, thus allowing faster and moreaccurate writing of data on the media. This is possible because theinducement of sufficient magnetic flux requires substantially lessenergy input. As such, the rise time of the written pulse issubstantially shortened. Thus allowing for a sharper written transitionin the media.

The above description relates to the general fabrication of a highlyefficient surface thin film magnetic recording head according to theteachings of the present invention. That is, by using the columned (orcombed) structure for the body of the head which reduces the overallinductance of the head, and by applying back-bars 40 which reduces thereluctance, an improved head is necessarily formed. In addition thereare various other parameters which can be modified to apply the head ofthe present invention to a wide variety of writing functions. It shouldbe noted that simply using a combed or columned structure in and ofitself produces a better, more efficient head. Likewise, the use ofback-bars 40 is also independently advantageous and can be utilized onheads having a combed or non-combed core, as efficiency will beincreased in both cases.

Referring to FIGS. 12 and 13, two substantially completed heads 46 areshown. In FIG. 12, head 46 is a multi-channel head having fiveindependent channels. That is, each channel can be individuallytriggered and caused to write independent of the other four channels. Toaccomplish this, each back-bar 40 has its own coil 44 wrapped about it.In a variety of known ways, these coils 44 can be coupled to acontroller and appropriately driven. In FIG. 13, the back-gaps 40 areconfigured in the same way, however a single coil 44 is coupled to allof the back-gaps 40. In this way, when the coil is energized, thevarious channels will each write simultaneously. Any intermediatecombination is likewise achievable. That is, the individually wrappedcoils 44 (FIG. 12) can be tied together, achieving the same result asutilizing a single coil 44. Alternatively, any number or combination ofchannels can be coupled mechanically or electrically together. In thisembodiment, each back-bar 40 is sized to correspond to an individualchannel. As discussed, these back-bars 40 can then be separately woundor wound as a single unit.

An additional advantage of separately driving each channel individually,is the ability to fine-tune each channel. As is known in the art and isgenerally represented by an “I-Sat” curve, each head and moreparticularly each channel may saturate at slightly different levels ofampere-turns. Therefore, it is desirable to select a particular level ofcurrent input to maximize the efficiency and output of each channel.This optimal value may very slightly from channel to channel. As such,by performing this evaluation for each channel, the optimal currentinput for each channel can be determined. This information is moot inthose heads where all the channels are driven by a single coil. However,with independently driven channels, each channel may be driven at itsoptimal level of ampere-turns.

The head 46 of the present invention has been shown to have fivechannels. Any number of servo channels could be so fabricated. Fivechannel or two channel heads seem to be an industry standard for themoment.

The choice to produce a multi-channel head having independent channelsor one having its channels tied together also affects the application ofthe thin film 34 to the tape bearing surface of the head 46. Morespecifically, a multi-channel head having independently driven channelsmay need to have those channels magnetically isolated from one anotherto avoid cross talk, depending upon the timing of the information beingwritten.

When cross talk is not an issue, the surface thin film layer 34 canextend across the entire surface of the head, producing a unitary sheetfilm. However, the areas of sheet film between the channels may not bewell saturated, due to the limited width of the channels and hence thedriven core(s), in relation to the overall area of the sheet film. Thus,the areas of sheet film between adjacent channels will provide anundesirable high permeable flux leakage path which limits the amount ofsignal flux actually passing across the writing gaps 36 thus resultingin a non-linear output from a servo read head as a function of positionalong the servo band. Hence, even when cross-talk is not an issue, thepreferred embodiment of the low inductance, multi-channel timing basedservo head of the present invention will include a separate thin filmlayer 34 that is dedicated to a single channel and is magneticallyisolated from the adjacent channels. The process of providing channelseparated thin film 34 areas is discussed below.

In addition, the application of the thin film 34 affects the creation ofthe air bleed slots 38. Namely, if the slots 38 are cut into the head 46after the thin film 34 has been deposited, rough corners may be producedwhich negatively affects the interaction between the head 46 and themedia. If the thin film 34 is deposited after the slots are cut, thinfilm step coverage and adhesion over the slots becomes yet anotherissue.

The present invention contemplates a variety of techniques to deal withthe above mentioned considerations. The particular technique selectedwill also depend on the method used to form the writing gaps 36 into thethin film layer 34.

FIG. 14 represents the simplest head fabrication format. Here, head 46is a multi-channel head wherein the various channels are all coupledtogether. Though not shown, the gaps 36 will be patterned into eachchannel above the ceramic member 14 (i.e., that of FIG. 13). Thin filmlayer 34 (designated by the hash lines) has been deposited over theentire surface of head 46. As discussed above, this makes the cutting ofair bleed slots 38 problematic. However, this problem can be reduced byslitting the heads prior to applying the film. As such, a relativelyhigh quality head 46 can be produced. The advantage of such anarrangement is that the thin film layer 34 provides a uniformtape-bearing surface over the entirety of the upper surface of head 46.Conversely, the photolithography becomes more difficult due to thepresence of these slots.

FIG. 15 represents a modified embodiment of a multi-channel head whereinthe channels are all coupled together. Once again, cross talk betweenchannels is not an issue. Here, thin film layer 34 is contained betweenupper and lower bounds defined by air bleed slots 38. This arrangementavoids the above discussed issue of cutting through the thin film layer34 or depositing the thin film layer 34 over existing air bleed slots38. The production of this thin film 34 pattern can be accomplished invarious ways. For example, prior to creating air bleed slots 38, a thinfilm 34 could be deposited over the entire upper surface of head 46.Then, areas of that thin film could be removed; leaving only the areadesignated in FIG. 15. This deposition could be selectively defined by aselective plating or a selective sputtering process used with theappropriate masks, or the film could be selectively removed afterdeposition, using any known technique.

Turning to FIG. 16, thin film layer 34 can also be configured for usewith magnetically isolated channels. Primarily, this accomplished byceramic sections 32A-32E. However, if thin film layer 34 were continuousfrom one channel to the next, cross talk would occur, thus eliminatingthe ability to independently control the channels in so much asnon-linear results will occur due to the flux leakage. As such, with anyindependently driven, multi-channel head 46, the magnetically permeablethin film layer 34 must be absent between the various channels. Thepattern 48 of thin film 34 (covering channels 1 and 2) in FIG. 16,illustrates the simplest way of accomplishing this. A strip 50 is devoidof the thin film 34, over the entire length of the head. In thisarrangement, the remaining thin film layer 34 extends across the airbleed slots 38. Strip 50 can be formed by preventing the deposition ofthe thin film 34 in this area during formation, i.e., platting orlithography, or by removing it after its application. The minimum widthof strip 50 is determined by the minimum barrier required to preventmagnetic coupling and depends on the specific parameters of thecompleted head 46. This embodiment has the advantage of maintaining alarge film surface which may be advantageous in minimizing the wear ofthe surface film and thus increase the lifetime of the head.

Alternatively, elimination of areas of thin film 34 between adjacentchannels is advantageous in that it eliminates a high permeability fluxleakage path that limits the flux across the writing gaps. Hence,elimination of the surface film between the channels will provide forthe maximization of magnetic flux flowing uniformly across the writinggaps 36.

Channel 3 is shown devoid of a thin film layer 34 for ease ofillustration. Writing gaps 36 simply illustrate their position, if thinfilm layer 34 were present. Channels 4 and 5 have thin film layer 34applied over them by pattern 52. Here, pattern 52 is contained withinthe air bleed slots 38, while also providing adequate channelseparation. Pattern 52 illustrates that smaller areas of thin film layer34 are sufficient to accomplish the completion of the head 46. FIG. 17illustrates a furtherance of this concept. Specifically, channel 1 showsan approximation of what would be the minimal acceptable amount ofcoverage for thin film layer 34. Here, thin film layer 34 is justsufficient to contact each pole of ferrite column 16A. The amount ofcontact need only be sufficient to allow the generated magnetic flux toenter and pass through thin film layer 34. The width of thin film layer34 is shown to be contained within glass beading 33. This width could bereduced further, however the minimum width must be sufficient to allowfor writing gaps 36. Though such further minimization is possible, it isoptimal to have thin film layer 34 at least equal the width of theferrite poles 16A to assure proper flux transfer and to prevent theexposure of the corners of ferrite column 16A. For purposes ofpatterning the channel width of thin film 34, the relevant edges can bedefined to be approximately equal to the width of the distance fromglass bond 33 from one side to the other. That is, the channel widthwill fall just inside of or just outside at the glass bonds. Channel 2is devoid of thin film layer 34 (for ease of illustration), whilechannels 3-5 show other patterns which are possible. Virtually any sizeor shaped pattern could be obtained, so long as sufficient channelseparation occurs.

Though various patterns are achievable, certain factors will determinewhich patterns are preferable for any given head 46. To illustrate thesefactors it should be understood that the thin film 34 layer serves adual purpose. First, it completes a magnetic circuit by couplingtogether the poles in the ferrite columns (with or without theadditional consideration of channel separation). Second, the thin filmlayer 34 acts as a tape bearing surface as the media is pulled acrossthe recording head 46. As such, the minimum amount of coverage providedis limited by what is acceptable to create the magnetic circuit.Ultimately, the maximum amount could encompass the entire upper surfaceof the recording head 46. In some cases, such maximized coverage may beacceptable. As discussed, it is often desirable to avoid any interactionbetween the thin film layer 34 and the air bleed slots 38. Then, themaximum amount of coverage is defined by the distance D (FIG. 17)between the innermost air bleed slots 38.

An additional consideration arises when an edge (E1-E4) of the thin filmlayer 34 is located within the area defined by distance D and the widthof the head 46. Namely, the media will strike or engage that surfaceE1-E4 as it moves across the head 46. This is normally not aconsideration when the thin film 34 covers the entire head 46 becausethe edge of the head is by the media. When an edge E1-E4 is locatedcloser to the gaps 36 located over ceramic member 14, and the mediaengages this edge at speed, it may be caused to skip or jump away fromthe head 46. This issue is problematic if it is random and unpredictableand/or if the media does not reengage the head prior to the writing gaps36. Obviously, if it skips the writing gaps 36 the media cannot beproperly written. Therefore, if an edge E1-E4 is to occur, it ispreferable that it occurs further from the writing gaps 36 occurringover ceramic member 14, as illustrated in channel 5, by edge E4. In thislocation, if skipping or jumping occurs, the media has a longer distanceto correct itself. This self-correction may also be aided by thecurvature of the head 46. Furthermore, the pattern shown by channels 4and 5 is also advantageous in that a majority of the material transitionregions are covered by the thin film 34, thus preventing them fromdamaging or inappropriately writing the media. The transition regionsinclude the transition from ceramic to glass, from glass to ferrite, andfrom ferrite to ceramic.

To create the various patterns of thin film layer 34, any known methodof generating and defining a thin film can by utilized. For example,larger areas can have a thin film deposited on them and then wet etchingor ion milling can be used to remove sections. Such techniques are wellknown and relatively easy to perform.

In operation, magnetic recording head 46 is secured to an appropriatehead mount. Magnetic tape is caused to move over and in contact with thetape-bearing surface of the head 46. At the appropriate periodicinterval, electrical current is caused to flow through the coils 44. Asa result, magnetic flux is caused to flow through the back-bar 40,through the ferrite columns 16A-16E, and through the magnetic thin film34 (as the ceramic member 14 minimizes a direct flow from one pole ofthe ferrite column 16A-16E to the other, causing the magnetic flux toshunt through the permeable magnetic film). As the magnetic flux travelsthrough the magnetic thin film 34, it leaks out through the writing gaps36, thus causing magnetic transitions to occur on the surface of themagnetic tape, in the same pattern and configuration as the gaps 36itself.

The above head fabrication process has been described with respect to amagnetic recording head employing a timing based servo pattern. However,the process could be applied equally well to any type of surface filmrecording head.

The present disclosure presents a plurality of elements and conceptswhich work in a synergistic arrangement to arrive at a highly efficientsurface film magnetic recording head. It is to be understood that thesevarious elements and concepts can be effectively utilized alone or inother combinations than disclosed while still remaining within thespirit and scope of the present invention. Namely, using a columned orcombed head member in and of itself produces a higher quality and moreefficient head. Similarly, removing the high reluctance back-gap andreplacing it with one or more magnetically permeable back-bars leads toa better and more efficient surface film-recording head. Utilizing boththe combed structure and back-bars produces an optimal head, achievingsynergistic results. Finally, utilizing a specific pattern ofmagnetically permeable thin film to isolate the channels and to act asthe tape bearing surface, can be used alone or in combination with theabove aspects of the present invention to arrive at a superior recordinghead.

Comparing two heads, each wound with two turns of wire and driven by thesame single channel drive circuit, the head pursuant to this invention(FIG. 13) exhibits a current rise time in the 20 nanosecond range whilethe high inductance head made pursuant to the Albrecht et al. patent(FIG. 18) exhibits current rise time in the 50 nanosecond range. Thecorresponding inductances were measured to be about 250 nH and 700 nH,respectively, for the two heads. The shorter rise time correspondsroughly to the L/R time constant of the head as a circuit element. Hencethe low inductance magnetic recording heads of the present invention arecapable of recording timing based signals on media resulting in sharpermagnetic transitions than media written with previously known heads. Asa result, both the heads produced and the media written by those headswill perform significantly better than the prior art heads and the mediaproduced by them. With due consideration to the details of the writecircuitry, one can expect to at least double the bandwidth by the use ofthe low inductance head of the present invention. Even more dramaticresults can be expected with the independently driven, multi-channel lowinductance head, as illustrated in FIG. 12, while taking into accountthe limitations and expense of the multi-channel drive circuitry.

In accordance with the above teachings, FIG. 19 illustrates a crosssection of a thin film magnetic recording head 100 having two isolatedchannels 110, 120. Though channels 110, 120 are physically isolated fromone another, they are not magnetically isolated because magneticallypermeable thin film layer 130 is continuous and covers both channels110, 120. This configuration is advantageous in that is provides asmooth and continuous tape bearing surface. Thus, headwear will likewisebe even. Furthermore, there will be exemplary interaction between themedia and the tape-bearing surface. The disadvantage is that channels110, 120 are not magnetically isolated. As explained above, themechanical advantages of a continuous magnetically permeable surface canproduce poor magnetic results due to the leakage of flux into theinterchannel area.

To optimally drive each channel, thin film layer 130 can be removed (orselectively applied) to arrive at a pattern similar to that illustratedin FIG. 20. Here, thin film layer 100 only exists in a region above eachchannel 110, 120. The specific size and shape of these patterns was alsodescribed in detail above. This solution provides excellent magneticisolation, however it generates spaces or voids 140. More specifically,voids 140 are the spaces between the remaining thin film 130 as theyextend from the upper surface 150 of the head substrate.

Though the components illustrated in FIG. 20 are not to scale in generalor with respect to one another, it does illustrate how voids 140 couldbe problematic. As the flexible media travels at speed across head 100,portions of the media can sag into voids 140 which may affect thecontact between the media and the writing gaps. Furthermore, with theseuneven surfaces and differing degrees of contact, film wear is increasednear the edges of the film channel where higher contact forces exist.Finally, causing the media to contact these uneven surfaces couldpossibly damage the media.

FIG. 21 illustrates one solution to this problem. Magnetically permeablethin film 130 exists in a layer having a predetermined thickness aboveeach channel 110, 120. Wear pads 160 also having the same predeterminedthickness are formed over much of the remaining surface. Wear pads 160are formed from the same magnetically permeable thin film material asthin film 130. Voids 140 still exist, but they are much smaller andpresent much less of a problem when the media contacts the thin filmlayer. That is, the wear pads 160 and the thin film 130 approximate acontinuous surface. As compared to the embodiment illustrated in FIG.20, a majority of the space defined by voids 140 has been filled in withthin film wear pads 160. The remaining voids (FIGS. 21 and 22) are stillsufficient to provide magnetic isolation between channels whileproviding a larger surface area over which the media is able touniformly contact. Since the material is the same, wear will be evenacross the entirety of the head. Since the magnetic media or tape issignificantly stiff, it will not sag into the voids. The voids can haveany spacing, but will typically be between 1-30 microns wide.

One process of forming the embodiment illustrated in FIGS. 21-22 isillustrated in FIGS. 23-25. Referring to FIG. 23, a magneticallypermeable thin film layer 200 is evenly deposited over an upper surfaceof head substrate 210. Photoresist 220-224 is patterned on top of thinfilm layer 200. As illustrated in FIG. 24, head substrate 210 issubjected to an etching process such as ion milling or a chemicaletching process (wet etching). As a result, exposed portions of thinfilm layer 200 are removed, creating voids 230-235. In FIG. 25, theremaining photoresist 220-224 is washed away or otherwise removed. Whatremains is head substrate 210 having channels 240, 250 with magneticallypermeable thin film layer 200 having been sectioned to provide wear pads260, 261 and 262 and writing channels 270, 271. Wear pads 260, 261 and262 and writing channels 270, 271, having been formed from the uniformthin film layer 200 have the same height and material characteristics.Magnetic isolation is achieved because of voids 230-235, whichmagnetically separate channels 240, 250 while still providing arelatively large tape bearing surface. It should be noted that more orless channels could actually be utilized. Voids 230 and 235, if actuallylocated at the endpoints of head substrate 210 need not be present. Thatis, wear pads 260 and 262 could extend to the ends of head substrate210.

When the voids 140 between the film sections are relatively narrow, thestiffness of the media will lower the contact pressure on the channeledges as compared to the case of no wear pads. In summary, wear pads 160in conjunction with relatively narrow voids 140 will approximate acontiguous tape bearing surface that also retains the full character ofmagnetically isolated channels

The above embodiment is advantageous in that it is relatively easy tomanufacture, provides more even media-bearing surface, and has moreuniform wear characteristics. Voids 230-235 do still exist however, andmay be able to affect the media. To prevent this from occurring, FIGS.26-27 illustrate yet another embodiment. In essence, voids 230-235 havebeen “filled in” with a magnetically impermeable material to a heighteven with or slightly less than the magnetically permeable thin film260-262. The non-magnetically permeable spacers 280-285 can be formedusing a lift-off technique. Spacers 280-285 provide magnetic isolationbetween channels 240, 250. They also provide an even, consistent, andcontinuous tape-bearing surface. The material can be chosen to havesimilar wear characteristics to that of the magnetically permeable thinfilm so that over time, degradation caused by media interaction isfairly uniform.

To form this embodiment, a uniform magnetically permeable thin filmlayer 200 is deposited on head substrate 210 as illustrated in FIG. 28.Photoresist patterns 220-224 are applied atop thin film layer 200. Thisstructure is then etched so that portions of thin film layer 200 areremoved leaving voids 230-234, as illustrated in FIG. 29. Then amagnetically impermeable material 290 is uniformly applied to theexposed surfaces, as illustrated in FIG. 30. Photoresist 220-224 is thenwashed away, taking with it portions of impermeable material 290. Whatremain are non-magnetically permeable spacers 280-285 as illustrated inFIG. 31. Because of the accuracy of the deposition techniques, spacers280-285 are generally equal in height to the magnetically permeablematerial 260, 261, 263, 270, and 271 so as to form an even andcontinuous tape-bearing surface.

FIGS. 32 and 33 illustrate a variation of the embodiment illustrated inFIG. 26. A continuous tape-bearing surface is provided howevermagnetically permeable areas 300, 310 only exist over each of thechannels. The remainder of the tape-bearing surface is comprised ofnon-magnetically permeable spacers 320, 330, 340. The lift off techniqueis again utilized, as illustrated in FIG. 34-37. A magneticallypermeable thin film layer 200 is deposited on head substrate 210.Photoresist patterns 350, 360 are then applied above each channel 240,250. The exposed portions of thin film layer 200 are then etched away. Amagnetically impermeable layer 370 is then applied across the entireexposed surface. Finally, photoresist patterns 350, 360 are washed awayleaving an even and continuous tape-bearing surface.

FIG. 38 illustrates a portion of a single channel and is generallyreferred to as 400. Channel portion 400 includes ferrite portions 405,410, ceramic gap 415 and ceramic spacers 420, 425 as described above. Ofcourse other materials having the appropriate magnetic characteristicscould be utilized instead. Above some or all of this structure, amagnetically permeable thin film (not illustrated) is deposited. Writinggaps 430 are illustrated where they would be located if the thin filmwere present. Glass bonds 435, 440 connect ferrite portions 405, 410 toceramic spacers 420, 425 while providing a barrier between them.

When the thin film is in place, a magnetic circuit is formed. Magneticflux moves from ferrite portion 405, through the thin film layer andinto ferrite portion 410 (or it could travel in the opposite direction).As it passes through the thin film layer, flux leakage through writinggaps 430 will write a pattern on the tape or other media as it passesclose by. Ideally, a uniform flux density is achieved across the widthof channel 400 (left to right, as illustrated). If this occurs, thewritten pattern will likewise be uniform.

The uniformity of the magnetic flux will be determined by the thin filmlayer where two competing considerations must be taken into account. Inthe present case, we are concerned with a magnetically isolated channel400. Thus, the thin film layer cannot form a continuous path to anyadjacent channel (not illustrated). Therefore, the first considerationis to determine how wide (from left to right, as illustrated) to limitthe thin film layer. All that is required for magnetic channelseparation is relatively narrow zone absent of magnetically permeablethin film. While, achieving channel separation such a wide thin filmlayer would allow for leakage around writing gap 430. Depending upon theconfiguration of writing gap 430, 431 (FIGS. 38 and 39), this fluxleakage would be more or less problematic. The symmetrical writing gap430 would result in symmetrical flux leakage about either side of it.However, an asymmetrical writing gap 39 would have more flux leakagewhere the separate gaps are closer (left side, as illustrated) thanwhere they are spaced apart. Thus, uniformity of the flux across thewidth of writing gap 431 would not be achieved. In both cases, fluxdensity across the gap would be decrease when flux leakage is permitted.

Thus, flux leakage around writing gaps 430, 431 is undesirable. Sinceflux leakage is facilitated by having a wider thin film layer,decreasing the width of this layer will minimize the problem. However,the second consideration is that making the thin film layer too narrowcould expose ferrite portions 405, 410 and in particular ferrite corners445. Ferrite corners 445 are local maximums and can-write the media ifexposed. This may or may not be acceptable to the media manufacturer orthe drive system manufacturer. Thus, at a minimum the thin film layershould have a width of W2 to prevent exposure of any portion of ferriteportions 405, 410.

As media passes over channel portion 400 (top to bottom or vice versa asillustrated), there can be lateral wear of the thin film layer. That is,the edge of the thin film layer parallel to glass bonds 435, 440 willwear away over time. Therefore, it is preferable not to have the thinfilm layer equal to the width W2, but rather greater than it. Ideally,the width of the thin film layer will fall between width W1 and widthW2. This will reasonably limit flux leakage while preventing exposure offerrite portions 405, 410, both when newly constructed and after acertain amount of lateral wear has occurred.

FIG. 40 illustrates a furtherance of this concept. Here, thin film layer450 is illustrated and has a maximum width equal to W1 (FIG. 38) and aminimum width equal to W2. More specifically, sections 455, 460 havebeen removed from thin film layer 450 over ceramic gap 415. Sections455, 460 prevent substantially any flux leakage from occurring aroundwriting gap 430. However, this minimization only occurs over ceramic gap415 so that ferrite portions 405, 510 are fully covered and excessmaterial is provided to account for lateral wear.

As described above, it may be desirable to deposit magneticallyimpermeable material on the head substrate in those areas where thinfilm layer 450 is absent. In that regard, sections 455, 450 could belikewise filled in to provide a smooth and continuous tape bearingsurface with thin film layer 450. In addition, this would preventlateral wear from encroaching on writing gap 430. As also discussed ingreater detail above, the height (as illustrated) of the thin film layercan be varied. Voids in this direction could also be filled with amagnetically impermeable material.

FIG. 40 also illustrates another concept. Writing gaps 30 areillustrated in a particular timing based pattern. Writing gaps 30 extendthrough the surface of thin film layer 450. Thus, as flux passes throughthin film layer 450, a portion thereof escapes through gaps 130 andwrites any magnetic media in proximity thereto. These gaps 130 aretherefore open and debris can accumulate within them.

The previous sections above describe, in general, providing a smooth andcontinuous tape-bearing surface with and/or around thin film layer 450.It may also be advantageous to fill in writing gaps 130 withnon-magnetically permeable material to prevent the accumulation ofdebris. This can be accomplished through a variety of techniques. In oneparticular application, a Focussed Ion Beam (FIB) can be used toprecisely deposit material within writing gaps 130 to provide a smoothand continuous tape-bearing surface. The FIB may be used to initiallycut writing gap 130 through thin film layer 450 as well. The use of aFIB to fill in material is advantageous because of the precision that isachievable. To that end, reference is made to application Ser. No.09/255,762, filed Feb. 23, 1999, which is herein incorporated byreference in its entirety.

One aspect of the present invention provides for forming an even andsupportive media bearing surface that still allows for the magneticisolation of the independent channels. This can be accomplished byleaving sufficient space to provide magnetic isolation while maximizingthe area of the tape-bearing surface. Alternatively, magneticallyimpermeable material can be utilized to form a continuous surface. Toproduce these configurations, a variety of techniques can be utilized toappropriately apply and/or remove the various thin film materials. Itshould also be appreciated that the disclosed techniques can be utilizedon magnetic heads having any number of channels.

While the present application has been described with reference tospecific material that may be added to a substrate to reduce oreliminate gaps or space and the use of photoresist has been discussed asa masking layer, these materials are not meant to be limiting. That is,various other materials can be utilized as desired to reduce oreliminate the gaps or spaces. In addition, materials other thanphotoresist can be used to define a pattern and as a masking layer, solong as the material can be appropriately applied and subsequentlyremoved without damaging the substrate.

Those skilled in the art will further appreciate that the presentinvention may be embodied in other specific forms without departing fromthe spirit or central attributes thereof. In that the foregoingdescription of the present invention discloses only exemplaryembodiments thereof, it is to be understood that other variations arecontemplated as being within the scope of the present invention.Accordingly, the present invention is not limited in the particularembodiments which have been described in detail therein. Rather,reference should be made to the appended claims as indicative of thescope and content of the present invention.

1-4. (canceled)
 5. A magnetic recording head formed by the method ofclaim
 1. 6. Magnetic tape written by the magnetic recording head ofclaim
 5. 7. A multi-channel magnetic recording head, comprising: a headsubstrate having a plurality of channels; and a magnetically permeablethin film layer on a surface to the head substrate, having at least onevoid so as to magnetically isolate at least one of said plurality ofchannels from at least one other of said plurality of channels. 8.Magnetic recording media written by the head of claim
 7. 9. A method ofmaking a multi-channel magnetic recording head, comprising: forming amagnetically permeable thin film on a head substrate; forming at leastone void through the thin film in-between at least two channels; andplacing a magnetically impermeable material into the void.
 10. Themethod of claim 9, wherein voids are formed so as to isolate each of thechannels.
 11. The method of claim 9, wherein forming at least one voidincludes: removing the thin film in all areas except directly over eachchannel of the head substrate.
 12. The method of claim 11, wherein eachchannel is defined by a width of a magnetically permeable materialwithin the head substrate.
 13. The method of claim 11, wherein eachchannel is defined by a width of a magnetically permeable materialwithin the head substrate plus a width of a bonding material joining themagnetically permeable material to a remainder of the head substrate.14. The method of claim 9, wherein forming the void includes: applyingphotoresist over the thin film in a pattern defining a position of thevoid; and etching the thin film in areas exposed by the photoresist. 15.The method of claim 14, wherein placing the magnetically impermeablematerial includes; applying the magnetically impermeable material overthe photoresist and the voids; and removing the photoresist and themagnetically impermeable material attached thereto.
 16. The method ofclaim 14, wherein the magnetically impermeable material has a heightsubstantially equal to a height of the thin film.
 17. A magneticrecording head formed by the method of claim
 9. 18. Magnetic mediawritten by the recording head of claim
 17. 19. A multi-channel magneticrecording head, comprising: a multi-channel head substrate; amagnetically permeable thin film layer located on the head substrate andincluding a writing gap for each channel; and a magnetically impermeablemember dividing the thin film layer into magnetically isolated regions.20. The magnetic recording head of claim 19, wherein the magneticallypermeable thin film layer and the magnetically impermeable member form asubstantially smooth and substantially continuous tape bearing surface.21. The magnetic recording head of claim 19, wherein a height of thethin film layer is substantially equal to a height of the magneticallyimpermeable member.
 22. The magnetic recording head of claim 19, whereinthe thin film is only located above each of the channels on a writingside of the head substrate and a remainder of a surface of the headsubstrate on the writing side is covered with sections of themagnetically impermeable member.
 23. The magnetic recording head ofclaim 18, wherein each channel is defined by a width of a magneticallypermeable material within the head substrate.
 24. The magnetic recordinghead of claim 22, wherein each channel is defined by a width of amagnetically permeable material within the head substrate plus a widthof a bonding material joining the magnetically permeable material to aremainder of the head substrate.
 25. The magnetic recording head ofclaim 22, wherein ferrite corners in each channel are covered by themagnetically permeable thin film.
 26. The magnetic recording head ofclaim 19, wherein a magnetically impermeable member is located betweeneach channel in the thin film layer so as to magnetically isolate eachchannel from one another.
 27. The magnetic recording head of claim 26,wherein a width of each magnetically impermeable member is a minimumrequired to provide magnetic isolation.
 28. The magnetic recording headof claim 19, wherein the writing gap is filled with magneticallyimpermeable material. 29-32. (canceled)
 33. A magnetic recording headformed by the method of claim
 29. 34. Magnetic tape written by themagnetic recording head of claim
 33. 35. A method of making amulti-channel magnetic recording head, comprising: forming amagnetically permeable thin film on a head substrate; forming at leastone void through the thin film in-between at least two channels; andplacing a magnetically impermeable material into the void, whereinforming at the least one void includes applying a mask over the thinfilm in a pattern defining a position of the void and etching the thinfilm in areas left exposed by the mask.
 36. The method of claim 35,wherein placing the magnetically impermeable material includes applyingthe magnetically impermeable material over the mask and the voids, andremoving the mask and the magnetically impermeable material attachedthereto.